13-8Mo XM-13 S13800 is a martensitic precipitation hardening stainless steel capable of high strength and hardness along with good levels of resistance to both general corrosion and stress-corrosion cracking. In addition, the alloy exhibits good ductility and toughness in large sections in both the longitudinal and transverse directions. Stainless steel 13-8Mo has been used for valve parts, fittings, cold-headed and machined fasteners, shafts, landing gear parts, pins, lock washers, aircraft com
17-4 PH SUS630 S17400 DIN1.4462) is a precipitation hardening martensitic stainless steel with Cu and Nb additions. This material combines high strength and hardness, with good corrosion resistance. Mechanical properties can be optimized with heat treatments. The materials are generally used for parts requiring corrosion resistance and high strength at room temperature. It is suitable for machining in the solution-annealed, cold-worked and age-hardened condition. Standard: ASTM A564, A705, A69
Paslanmaz Celik Rulo, Paslanmaz Celik Sac, Paslanmaz Celik Boru, Paslanmaz Celik Profil, Paslanmaz Celik Cubuk, Paslanmaz Celik Lama, Paslanmaz Celik stainless steel products, stainless steel profile, stainless steel pipe, stainless steel plate, stainless steel welded pipe, europe welded pipe, stainless steel drawn pipe, stainless steel metal sheet, stainless steel bracket, stainless steel square profile, stainless steel rectangle profile, stainless steel polished pipe, stainless steel fitt